Silver (Solder) Brazing Alloy
Silver (Solder) Brazing Alloys are commonly used in many metal-joining applications. Properly used they give a clean joint, which will be stronger than the metals being joined. Because of the capillary action used the alloy is drawn into the joint and leaves minimal alloy outside for cleaning, although flux residue will still need to be removed.
Alloy |
Ag ± 1 |
Cu ± 1 |
Zn ± 1 |
Cd ± 1 |
Others |
Solidus/ Liquidus °C |
Brodon 60C |
60 |
28 |
11.5 |
0.5 |
|
680/710 |
Brodon 50C |
50 |
15 |
18 |
17 |
|
620/640 |
Brodon 50CN3 |
50 |
15.5 |
15.5 |
16 |
Ni 3 |
645/690 |
Brodon 45C |
45 |
17 |
18 |
20 |
|
605/620 |
Brodon 42C |
42 |
17 |
16 |
25 |
|
610/620 |
Brodon 40C |
40 |
19 |
21 |
20 |
|
595/630 |
Brodon 40CS03 |
40 |
18.7 |
21 |
20 |
Si 0.3 |
595/630 |
Brodon 385C |
38.5 |
21.5 |
14.5 |
25.3 |
Si 0.2 |
605/650 |
Brodon 34C |
34 |
21 |
23 |
22 |
|
610/700 |
Brodon 30C |
30 |
27 |
22 |
21 |
|
600/690 |
Brodon 30CS03 |
30 |
26.7 |
22 |
21 |
Si 0.3 |
600/690 |
Brodon 27C |
27 |
28.5 |
23.5 |
21 |
|
615/690 |
Brodon 25C |
25 |
33 |
23 |
19 |
|
605/720 |
Brodon 212C |
21.2 |
31 |
32 |
15.6 |
Si 0.2 |
620/730 |
Brodon 20C |
20 |
40 |
29 |
11 |
|
605/765 |
Brodon 19C |
19 |
40.5 |
28 |
12.3 |
Si 0.2 |
660/750 |
Brodon 17C |
17 |
40 |
28.8 |
14 |
Si 0.2 |
610/780 |
Brodon 16C |
16 |
39.8 |
30 |
14 |
Si 0.2 |
605/780 |
Brodon 125C |
12.5 |
44.7 |
32.2 |
10.3 |
Si 0.3 |
605/790 |
Brodon 115C |
45.7 |
32.2 |
10.3 |
Si 0.3 |
11.5 |
605/780 |
Brodon 09C |
9 |
51.7 |
33 |
5.5 |
Si 0.3 |
625/830 |
Brodon 075C |
7.5 |
51.7 |
35 |
5.5 |
Si 0.3 |
630/780 |
Brodon 04C |
4 |
56 |
40 |
|
|
835/875 |
These alloys need to be used in well-ventilated areas (or within vacuum), as fumes may be dangerous. We also offer a comprehensive range of Cadmium free Alloys as a widely used alternative.
Brouwer Metaal Ireland Silver Brazing Alloys can be used to join a wide range of dissimilar metals such as steels, stainless steel, copper, copper alloys and tungsten carbides.
|
|
|
|